Precursors for silicon dioxide gap fill

ABSTRACT

A full fill trench structure is described, including a microelectronic device substrate having a high aspect ratio trench therein and filled with silicon dioxide of a substantially void-free character and substantially uniform density throughout its bulk mass. A method of manufacturing a semiconductor product also is described, involving use of specific silicon precursor compositions for forming substantially void-free and substantially uniform density silicon dioxide material in the trench. The precursor fill composition may include silicon and germanium, to produce a microelectronic device structure including a GeO 2 /SiO 2  trench fill material. A suppressor component may be employed in the precursor fill composition, to eliminate or minimize seam formation in the cured trench fill material.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a U.S. national phase under the provisions of 35 U.S.C. §371 of International Application No. PCT/US08/68521 filed Jun. 27, 2008, which in turn claims priority of U.S. Provisional Patent Application No. 60/946,968 filed Jun. 28, 2007 and U.S. Provisional Patent Application No. 61/055,809 filed May 23, 2008. The disclosures of such international application and U.S. provisional patent applications are hereby incorporated herein by reference, in their respective entireties, for all purposes.

FIELD OF THE INVENTION

The present invention relates to trench structures of microelectronic devices and methods for fabricating same, and to precursors having utility for forming silicon dioxide full-fill high aspect ratio trench structures in which the silicon dioxide precursor is flow filled in the trench and cures rapidly at low temperature to form silicon dioxide of a substantially void-free condition with substantially uniform density throughout its bulk volume.

DESCRIPTION OF THE RELATED ART

As dimensions in integrated circuits continue to decrease, correspondingly narrower trenches with increasing aspect ratios are required. Current processes to deposit silicon dioxide in trenches employ chemical vapor deposition. However, with technology nodes decreasing to below 65 nm, it becomes progressively more difficult to deposit silicon dioxide in narrow trenches without introducing voids in the deposited material.

Faced with such difficulty, a low-temperature flow-fill method in a controlled humidity environment or with an oxidant co-reactant is desired for curing, since elevated temperature hydrolysis and condensation reactions are prone to form voids and cracks in the product silicon dioxide material. Voids, cracks, and other defects in turn create inhomogenieties in the dielectric material that adversely affect device performance. A condensed matrix material that exhibits low shrinkage during thermal curing therefore is necessary in order to prevent cracking.

Uniform material densification in the narrow trenches is also a problem with conventionally available silicon dioxide precursors due to diffusion-limited oxidation that occurs during their curing.

Normally a high temperature (600-1200° C.) thermal anneal stage is used to form SiO₂. A low temperature process is preferred, due to high temperature incompatibilities with other structures, materials, and processes in the integrated circuit or memory device that lead to a degraded device with poor performance when high temperature annealing is employed. Further, high temperature annealing increases the overall thermal budget of the process, and is disadvantageous for such reason.

Conventional precursors used in the art to form oxide layers in semiconductors, which are characterized by the aforementioned problems, include: silane or methylsilane, as cured with hydrogen peroxide; polysilazane, as cured with ozone or oxic plasma; tetraethylorthosilicate, as cured with water; and hexachlorodisilane (HCDS), as cured with pyridine and water.

Although certain alkoxysilanes, such as triethoxysilane, have been utilized as silicon dioxide precursors, such precursors hydrolyze slowly in moist air and the condensation rate of silica at neutral pH is relatively slow. Precursors with hydrolyzable or labile groups can induce crosslinking, thereby generating a dense SiO₂ matrix with improved density, increased mechanical strength, and enhanced CMP (chemical mechanical polishing) and HF etch resistances. Even though water vapor annealing is effective for densifying the oxide film, in some integrations in which the transistor is formed before the isolation material is deposited, water annealing has the significant drawback that it causes oxidation around the transistor that degrades performance.

One possible composition for fill of memory device trenches is tetraethylorthosilicate (TEOS) as cured thermally with ozone, which holds the potential for achieving extremely conformal films. Such TEOS/ozone process, however, has the substantial deficiency that while the resultant composition can be made to fully fill the trench, it inherently leaves a seam where the growths from the trench sidewalls meet one another. This seam is a common weak region with enhanced removal rates when exposed to cleaning chemistries in subsequent device processing.

A precursor that can be flow-filled and hydrolyzed rapidly at low temperatures, then quickly condensed to form dense SiO₂ in the trench before the formation of a skin layer, would achieve a substantial advance in the art.

Another issue related to such trench filling is that although water vapor annealing

SUMMARY OF THE INVENTION

The present invention relates to microelectronic device trench structures and fabrication methods therefor, and silicon dioxide precursors suitable for forming silicon dioxide full-fill high aspect ratio trench structures in which the precursor is flow filled in the trench and cures rapidly at low temperature to form silicon dioxide of a substantially void-free condition with substantially uniform density throughout its bulk volume.

In one aspect, the invention relates to a full fill trench structure comprising a microelectronic device substrate having a high aspect ratio trench therein and a full filled mass of silicon dioxide in said trench, said silicon dioxide being of a substantially void-free character and having a substantially uniform density throughout its bulk mass.

In another aspect, the invention relates to a method of manufacturing a semiconductor product, including providing a microelectronic device substrate having a trench therein, and full filling the trench with a silicon dioxide precursor composition, and processing the silicon dioxide precursor composition to form a full fill mass of silicon dioxide in the trench, wherein the silicon dioxide precursor composition comprises a precursor silicon compound selected from the group consisting of:

(i) aminosilanes of the formula (R¹R²N)_(4-x)SiR_(x), wherein x is an integer having a value in a range of from 0 to 3, and each R, R¹, and R² is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl;

(ii) alkoxysilanes of the formula (RO)_(4-x)SiR¹ _(x), wherein x is an integer having a value in a range of from 0 to 3, and each R and R¹ is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl;

(iii) alkoxydisilanes of the formula (RO)_(3-x)R¹ _(x)Si—Si(OR)_(3-x)R¹ _(x) wherein x is an integer having a value in a range of from 0 to 2, and each R and R¹ is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (iv) aminodisilanes of the formula (R¹R²N)_(3-x)R_(x)Si—Si(NR¹R²)_(3-x)R_(x), wherein x is an integer having a value in a range of from 0 to 2, and each R, R¹, and R² is independently selected from among hydrogen, branched or unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (v) aminodisiloxanes of the formula (R¹R²N)_(3-x)R_(x)Si—O—Si(NR¹R²)_(3-x)R_(x), wherein x is an integer having a value in a range of from 0 to 2, and each R, R¹, and R² is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (vi) alkoxydisiloxanes of the formula (RO)_(3-x)(R¹ _(x)Si—O—Si(OR)_(3-x)R¹ _(x), wherein x is an integer having a value in a range of from 0 to 2, and each R and R¹ is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (vii) aminodisilazanes of the formula (R¹R²N)_(3-x)R_(x)Si—NH—Si(NR¹R²)_(3-x)R_(x), wherein x is an integer having a value in a range of from 0 to 2, and each R, R¹, and R² is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (viii) alkoxydisilazanes of the formula (RO)_(3-x)Si—NH—Si(OR)_(3-x)R_(x), wherein x is an integer having a value in a range of from 0 to 2, and each R and R¹ is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (ix) chloroaminosilanes of the formulae Cl_(4-x)Si(NR¹R²)_(x), wherein x is an integer having a value in a range of from 0 to 3, (R¹R²N)_(3-x)Cl_(x)Si—Si(NR¹R²)_(3-x)Cl_(x), wherein x is an integer having a value of 1 or 2, (R¹R²N)_(3-x)Cl_(x)Si—O—Si(NR¹R²)_(3-x)Cl_(x), wherein x is an integer having a value of 1 or 2, and (R¹R²N)_(3-x)Cl_(x)Si—NH—Si(NR¹R²)_(3-x)Cl_(x), wherein x is an integer having a value of from 1 or 2, and each R¹ and R² is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (x) cyclosiloxanes and cyclosilazanes of the formulae:

wherein n is an integer having a value in the range of from 0 to 4, and each R¹ and R² is selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, C₆-C₁₃ aryl, C₁-C₆ dialkylamino, and C₁-C₆ alkoxide; (xi) linear polysiloxanes and polysilazanes; (xii) silicon compounds of general formulae R_(4-x)SiL_(x) wherein x is an integer having a value of from 1 to 3, and L_(3-x)R_(x)Si—SiL_(3-x)R_(x), wherein x is an integer having a value of from 0 to 2, L is selected from isocyanato (NCO), methylethylketoxime (R¹R²C═N—O—), trifluoroacetate (CF₃OCO), triflate (CF₃SO₃), acyloxy (ROCO), β-diketonate (R¹COCHCOR²), β-diketiminate (R¹CNR²CHCOR³), β-diiminate (R¹CNR²CHCNR²R³), amidinate (RC(NR¹)₂), guanidinate {(R¹R²N)C(NR³)₂}, alkylamino (NR¹R²), hydride, alkoxide (RO), and formato (HCOO) and each R, R¹, R², and R³ is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (xiii) oxiranylsilanes of the formulae

wherein x is an integer having a value in a range of from 0 to 3, n is an integer having a value in a range of 0 to 3, and each R¹, R², and R³ is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, C₆-C₁₃ aryl, C₁-C₆ alkylamino, and C₁-C₆ alkoxide; (xiv) silicon precursors containing ethylacetate groups, of the formula (ROCOCH₂CH₂)_(x)Si(OR¹)_(4-x), wherein x is an integer having a value in a range of from 1 to 4, and each of R and R¹ is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (xv) (tBuHN)₂(H₂N)Si—Si(NH₂)(NHtBu)₂ wherein tBu is tertiary butyl; and (xvi) pre-polymer partial hydrolysis products of the foregoing compounds (i)-(xv).

In a still further aspect, the invention relates to a method of depositing silicon dioxide on a substrate, comprising contacting a substrate with a vapor of a precursor silicon compound selected from the group consisting of:

(i) aminosilanes of the formula (R¹R²N)_(4-x)SiR_(x), wherein x is an integer having a value in a range of from 0 to 3, and each R, R¹, and R² is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl;

(ii) alkoxysilanes of the formula (RO)_(4-x)SiR¹ _(x), wherein x is an integer having a value in a range of from 0 to 3, and each R and R¹ is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl;

(iii) alkoxydisilanes of the formula (RO)_(3-x)R¹ _(x)Si—Si(OR)_(3-x)R¹ _(x), wherein x is an integer having a value in a range of from 0 to 2, and each R and R¹ is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (iv) aminodisilanes of the formula (R¹R²N)_(3-x)R_(x)Si—Si(NR¹R²)_(3-x)R_(x), wherein x is an integer having a value in a range of from 0 to 2, and each R, R¹, and R² is independently selected from among hydrogen, branched or unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (v) aminodisiloxanes of the formula (R¹R²N)_(3-x)R_(x)Si—O—Si(NR¹R²)_(3-x)R_(x), wherein x is an integer having a value in a range of from 0 to 2, and each R, R¹, and R² is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (vi) alkoxydisiloxanes of the formula (RO)_(3-x)R¹ _(x)Si—O—Si(OR)_(3-x)R¹ _(x), wherein x is an integer having a value in a range of from 0 to 2, and each R and R¹ is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (vii) aminodisilazanes of the formula (R¹R²N)_(3-x)R_(x)Si—NH—Si(NR¹R²)_(3-x)R_(x), wherein x is an integer having a value in a range of from 0 to 2, and each R, R¹, and R² is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (viii) alkoxydisilazanes of the formula (RO)_(3-x)R¹ _(x)Si—NH—Si(OR)_(3-x)R¹ _(x), wherein x is an integer having a value in a range of from 0 to 2, and each R and R¹ is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (ix) chloroaminosilanes of the formulae Cl_(4-x)Si(NR¹R²)_(x), wherein x is an integer having a value in a range of from 0 to 3, (R¹R²N)_(3-x)Cl_(x)Si—Si(NR¹R²)_(3-x)Cl_(x), wherein x is an integer having a value of 1 or 2, (R¹R²N)_(3-x)Cl_(x)Si—O—Si(NR¹R²)_(3-x)Cl_(x), wherein x is an integer having a value of 1 or 2, and (R¹R²N)_(3-x)Cl_(x)Si—NH—Si(NR¹R²)_(3-x)Cl_(x), wherein x is an integer having a value of from 1 or 2, and each R¹ and R² is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (x) cyclosiloxanes and cyclosilazanes of the formulae:

wherein n is an integer having a value in the range of from 0 to 4, and each R¹ and R² is selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, C₆-C₁₃ aryl, C₁-C₆ dialkylamino, and C₁-C₆ alkoxide; (xi) linear polysiloxanes and polysilazanes; (xii) silicon compounds of general formulae R_(4-x)SiL_(x) wherein x is an integer having a value of from 1 to 3, and L_(3-x)R_(x)Si—SiL_(3-x)R_(x), wherein x is an integer having a value of from 0 to 2, L is selected from isocyanato (NCO), methylethylketoxime (R¹R²C═N—O—), trifluoroacetate (CF₃OCO), triflate (CF₃SO₃), acyloxy (ROCO), β-diketonate (R¹COCHCOR²), β-diketiminate (R¹CNR²CHCOR³), β-diiminate (R¹CNR²CHCNR²R³), amidinate (RC(NR¹)₂), guanidinate (R¹R²N)C(NR³)₂ alkylamino (NR¹R²), hydride, alkoxide (RO), and formato (HCOO) and each R, R¹, R², and R³ is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (xiii) oxiranylsilanes of the formulae

wherein x is an integer having a value in a range of from 0 to 3, n is an integer having a value in a range of 0 to 3, and each R¹, R², and R³ is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, C₆-C₁₃ aryl, C₁-C₆ alkylamino, and C₁-C₆ alkoxide; (xiv) silicon precursors containing ethylacetate groups, of the formula (ROCOCH₂CH₂)_(x)Si(OR¹)_(4-x), wherein x is an integer having a value in a range of from 1 to 4, and each of R and R¹ is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (xv) (tBuHN)₂(H₂N)Si—Si(NH₂)(NHtBu)₂ wherein tBu is tertiary butyl; and (xvi) pre-polymer partial hydrolysis products of the foregoing compounds (i)-(xv).

Another aspect of the invention relates to a method of forming an oxide material in a trench structure of a substrate for filling thereof, said method comprising depositing oxide precursor material on the substrate for filling of the trench structure, wherein the oxide precursor material comprises germanium and silicon.

A further aspect of the invention relates to a microelectronic device structure, comprising a substrate having a trench structure formed therein, wherein the trench structure is filled with a Ge/Si oxide composition.

In another aspect, the invention relates to a method of forming an oxide fill material in a trench, comprising depositing the oxide fill material from a precursor composition including a suppressor, to suppress seam formation.

Still another aspect of the invention relates to a method of suppressing adverse seam effects in fill of a trench structure of a substrate with a silicon material oxidizable to form silicon dioxide, said method comprising incorporating a germanium precursor in said silicon material.

The invention relates in another aspect to a microelectronic device structure, including a trench at least partially filled with a GeO₂/SiO₂ mixture.

Another aspect of the invention relates to a method of conducting a TEOS/O₃ process to fill a trench structure in a substrate, comprising adding a hydroxyl functional compound to said TEOS.

Yet another aspect of the invention relates to a method of filing a trench in a substrate, comprising carrying out a TEOS/ozone process to form silicon oxide material in the trench, with addition to the TEOS of an aldehyde.

A further aspect of the invention relates to a method of filing a trench in a substrate, comprising carrying out a TEOS/ozone process to form silicon oxide material in the trench, wherein TEOS is deposited in substrate in a composition comprising ethylene glycol and isopropyl alcohol.

Other aspects, features and embodiments of the invention will be more fully apparent from the ensuing disclosure and appended claims.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic representation of a high aspect ratio trench structure in which the trench contains silicon dioxide formed from a precursor of the present invention that is cured under low temperature conditions to yield silicon dioxide of a substantially void-free condition with substantially uniform density throughout its bulk volume, in the trench.

FIGS. 2 and 3 show schematic representations of a microelectronic device structure in which deposition of the trench-filling material is being carried out with suppressor in the deposited fill material, with FIG. 3 showing the effect of suppressor on growth of the oxide material in the trench.

DETAILED DESCRIPTION OF THE INVENTION, AND PREFERRED EMBODIMENTS THEREOF

The present invention relates variously to trench structures, and precursors and processes useful for forming such trench structures.

As used herein, “low temperature” means temperature below 400° C.

The term “flow fill” in reference to the precursor material of the present invention refers to material that in introduction to a high aspect ratio trench is self-leveling within the trench to form a bulk volume of the material in contact with the trench wall and floor surfaces.

The term “high aspect ratio” in reference to a trench in a microelectronic device substrate means a ratio of at least 3:1 of depth:width of the trench. In one preferred embodiment, the trench has a depth:width ratio in a range of from 3:1 to 10:1. In another preferred embodiment, the trench has a depth:width ratio of at least 5:1.

As used herein and in the appended claims, the singular forms “a”, “and”, and “the” include plural referents unless the context clearly dictates otherwise.

As used herein, the identification of a carbon number range, e.g., in C₁-C₆ alkyl, or C₁-C₁₂ alkyl, is intended to include each of the component carbon number moieties within such range, so that each intervening carbon number and any other stated or intervening carbon number value in that stated range, is encompassed, it being further understood that sub-ranges of carbon number within specified carbon number ranges may independently be included in smaller carbon number ranges, within the scope of the invention, and that ranges of carbon numbers specifically excluding a carbon number or numbers are included in the invention, and sub-ranges excluding either or both of carbon number limits of specified ranges are also included in the invention. Accordingly, C₁-C₁₂ alkyl is intended to include methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl and dodecyl, including straight chain as well as branched groups of such types. It therefore is to be appreciated that identification of a carbon number range, e.g., C₁-C₁₂, as broadly applicable to a substituent moiety, enables, in specific embodiments of the invention, the carbon number range to be further restricted, as a sub-group of moieties having a carbon number range within the broader specification of the substituent moiety. By way of example, the carbon number range e.g., C₁-C₁₂ alkyl, may be more restrictively specified, in particular embodiments of the invention, to encompass sub-ranges such as C₁-C₄ alkyl, C₂-C₈ alkyl, C₂-C₈ alkyl, C₃-C₅ alkyl, or any other sub-range within the broad carbon number range. It therefore is to be understood that any of the carbon numbers in the specified range may be selected as a respective lower limit or upper limit value of the number of carbon atoms in the specified substituent, so that all possible permutations of sub-ranges are to be regarded as being identically set forth herein.

In like manner, although a specific features, aspects, examples and embodiments are described in particular arrangements of the inventive subject matter, it is contemplated that such features, aspects, examples and/or embodiments may be selectively aggregated with one another, in permutations, combinations and sub-combinations thereof, within the contemplation and scope of the invention, and are to be regarded as being identically set forth herein.

The silicon dioxide precursors suitable for forming silicon dioxide full-fill high aspect ratio trench structures in the practice of the invention are flow tillable into high aspect trench structures and cure rapidly at low temperature to form silicon dioxide of a substantially void-free and crack-free condition with substantially uniform density throughout bulk volume of the cured silicon dioxide.

Precursors generally useful in the broad practice of the present invention include, without limitation, precursor silicon compounds selected from among the following:

(i) aminosilanes of the formula (R¹R²N)_(4-x)SiR_(x), wherein x is an integer having a value in a range of from 0 to 3, and each R, R¹, and R² is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl;

(ii) alkoxysilanes of the formula (RO)_(4-x)SiR¹ _(x), wherein x is an integer having a value in a range of from 0 to 3, and each R and R¹ is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl;

(iii) alkoxydisilanes of the formula (RO)_(3-x)R¹ _(x)Si—Si(OR)_(3-x)R¹ _(x), wherein x is an integer having a value in a range of from 0 to 2, and each R and R¹ is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (iv) aminodisilanes of the formula (R¹R²N)_(3-x)R_(x)Si—Si(NR¹R²)_(3-x)R_(x), wherein x is an integer having a value in a range of from 0 to 2, and each R, R¹, and R² is independently selected from among hydrogen, branched or unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (v) aminodisiloxanes of the formula (R¹R²N)_(3-x)R_(x)Si—O—Si(NR¹R²)_(3-x)R_(x), wherein x is an integer having a value in a range of from 0 to 2, and each R, R¹, and R² is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (vi) alkoxydisiloxanes of the formula (RO)_(3-x)R¹ _(x)Si—O—Si(OR)_(3-x)R_(x), wherein x is an integer having a value in a range of from 0 to 2, and each R and R¹ is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (vii) aminodisilazanes of the formula (R¹R²N)_(3-x)R_(x)Si—NH—Si(NR¹R²)_(3-x)R_(x), wherein x is an integer having a value in a range of from 0 to 2, and each R, R¹, and R² is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (viii) alkoxydisilazanes of the formula (RO)_(3-x)R¹ _(x)Si—NH—Si(OR)_(3-x)R_(x), wherein x is an integer having a value in a range of from 0 to 2, and each R and R¹ is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (ix) chloroaminosilanes of the formulae Cl_(4-x)Si(NR¹R²)_(x), wherein x is an integer having a value in a range of from 0 to 3, (R¹R²N)_(3-x)Cl_(x)Si—Si(NR¹R²)_(3-x)Cl_(x), wherein x is an integer having a value of 1 or 2, (R¹R²N)_(3-x)Cl_(x)Si—O—Si(NR¹R²)_(3-x)Cl_(x), wherein x is an integer having a value of 1 or 2, and (R¹R²N)_(3-x)Cl_(x)Si—NH—Si(NR¹R²)_(3-x)Cl_(x), wherein x is an integer having a value of from 1 or 2, and each R¹ and R² is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (x) cyclosiloxanes and cyclosilazanes of the formulae:

wherein n is an integer having a value in the range of from 0 to 4, and each R¹ and R² is selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, C₆-C₁₃ aryl, C₁-C₆ dialkylamino, and C₁-C₆ alkoxide; (xi) linear polysiloxanes and polysilazanes; (xii) silicon compounds of general formulae R_(4-x)SiL_(x) wherein x is an integer having a value of from 1 to 3, and L_(3-x)R_(x)Si—SiL_(3-x)R_(x) wherein x is an integer having a value of from 0 to 2, L is selected from isocyanato (NCO), methylethylketoxime (R¹R²C═N—O—), trifluoroacetate (CF₃OCO), triflate (CF₃SO₃), acyloxy (ROCO), β-diketonate (R¹COCHCOR²), β-diketiminate (R¹CNR²CHCOR³), β-diiminate (R¹CNR²CHCNR²R³), amidinate (RC(NR¹)₂), guanidinate (R¹R²N)C(NR³)₂ alkylamino (NR¹R²), hydride, alkoxide (RO), and formato (HCOO) and each R, R¹, R², and R³ is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (xiii) oxiranylsilanes of the formulae

wherein x is an integer having a value in a range of from 0 to 3, n is an integer having a value in a range of 0 to 3, and each R¹, R², and R³ is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, C₆-C₁₃ aryl, C₁-C₆ alkylamino, and C₁-C₆ alkoxide; (xiv) silicon precursors containing ethylacetate groups, of the formula (ROCOCH₂CH₂)₈Si(OR¹)_(4-x), wherein x is an integer having a value in a range of from 1 to 4, and each of R and R¹ is independently selected from among hydrogen, branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl; (xv) (tBuHN)₂(H₂N)Si—Si(NH₂)(NHtBu)₂ wherein tBu is tertiary butyl; and (xvi) pre-polymer partial hydrolysis products of the foregoing compounds (i)-(xv).

The above precursor compounds are readily synthesized within the skill of the art, for use in precursor compositions and applications of the present invention.

The precursor compositions of the invention in one specific aspect include aminosilanes, which hydrolyze rapidly in exposure to moisture, water and protic solvents. Ammonia, amines and disilanes can be employed to catalyze the condensation reaction, in the curing of the precursor composition. Precursors that form silyl radicals or ligands that readily undergo thermal decomposition (e.g. formate via decarboxylation of CO₂) are also included.

In another specific aspect of the invention, precursor compositions are employed, which include those of the formulae: (RO)_(4-x)SiH_(x), wherein x is an integer having a value of from 0 to 3, H_(4-x)Si(NR₂)_(x), wherein x is an integer having a value of from 1 to 4, H_(4-x)Si(NHR)_(x), wherein x is an integer having a value of from 1 to 4, (RO)_(3-x)H_(x)Si—Si(OR)_(3-x)H_(x), wherein x is an integer having a value of from 0 to 2, (NR¹R²)_(3-x)H_(x)Si—Si(NR¹R²)_(3-x)H_(x) wherein x is an integer having a value in a range of from 0 to 2, and each R, R¹, R² is independently selected from among hydrogen, and branched and unbranched C₁-C₆ alkyl.

In another aspect of the invention, precursor compositions are employed, which comprise silicon precursors in which the silicon atom is coordinated with ligands including at least one of isocyanato, methylethylketoxime, trifluoroacetate, triflate (F₃SO₃H), alkylamines, hydrides, alkoxides, disilanes, and formato. The resulting Si(OH)₄ sols can be condensed by various techniques, including for example: ammonia flow into the aqueous solution of the precursor; addition of co-reactants such as silicon tetrachloride, e.g., 0.05-5% SiCl₄, to an alkoxysilane (e.g., tetraethylorthosilicate (TEOS), dibutoxydiacetoxysilane (DBDAS), (EtO)₃SiH, etc.) to generate a small amount of an acid catalyst species; or addition of a silane (Si—H) or disilane (Si—Si) precursor such as hexaethylaminodisilane (HEADS).

Another approach to catalyzing condensation in a further aspect of the invention involves mixing a small amount of a chloroaminosilane, e.g., 0.05-5% Cl_(4-x)Si(NR₂)_(x), wherein x is an integer having a value in a range of from 1 to 3, to the corresponding aminosilane H_(4-x)Si(NR₂)_(x) wherein x has the same integer value of from 1 to 3.

In a similar manner, mixtures of chloro-substituted silanes and chloro-substituted disilanes can be added to alkoxysilane precursors in an amount, e.g., 0.05-5% by weight, based on the weight of the silicon dioxide precursor and the chloro compound, which is sufficient to generate catalytically effective species for the condensation reaction.

One preferred aminosilane precursor of the invention is hexaethylaminodisilane (HEADS), which rapidly condenses to SiO₂ in the presence of water or moisture. Other preferred alkylaminosilane precursors include (tBuHN)₂(H₂N)Si—Si(NH₂)(NHtBu)₂ and Si(NMe₂)₄.

One preferred group of silicon dioxide precursors of the invention includes the precursors (1)-(12) set forth below.

wherein OAc in formula (2) is acetoxy (CH₃C(O)O—), Me in formulae (3) and (4) is methyl, Et in formulae (1), (6), (7) and (11) is ethyl, tBu in formulae (2) and (5) is tertiary butyl, and R in the OR groups of formula (8) is branched or unbranched C₁-C₆ alkyl.

For efficient processing, the gap filling of the trench by flow fill techniques should be complete in a period of less than 10 minutes, preferably not exceeding five minutes, e.g., a period of 3-5 minutes.

The silicon dioxide precursor is deposited into the trench cavity by a full fill technique, such as chemical vapor deposition, atomic layer deposition, or other vapor-phase contacting of the substrate with the precursor, conducted at low temperature (<400° C.), preferably below 350° C., to cause the silicon dioxide precursor to enter and fill the trench. The precursor composition full filled in the trench is exposed to water or moisture and hydrolyzes, subsequently undergoing a condensation reaction to form the silicon dioxide product material.

The silicon dioxide material deriving from the precursor of the invention next is advantageously subjected to post-cure treatment, to effect densification of the silicon dioxide. The mass of silicon dioxide material in the trench constitutes a bulk mass that is in contact with the wall surfaces and floor surface of the trench, forming a continuous mass in the trench that is homogeneous and substantially void free in character.

Any suitable post-cure treatment may be employed for the formed silicon dioxide material in the trench to densify the silicon dioxide material that has been formed from the precursor by hydrolysis and condensation reactions. Specific post-cure treatment techniques that may advantageously be employed in specific embodiments of the invention include, without limitation, exposure of the flow filled material to oxygen, ultraviolet radiation, and/or low-temperature heating.

FIG. 1 is a schematic representation of a high aspect ratio trench structure including a silicon dioxide full filled trench, as formed by use of a precursor of the invention.

As shown in FIG. 1, the high aspect ratio trench structure 10 includes a microelectronic device substrate 12 with a top surface 14 and a bottom surface 16. The substrate includes a trench 18 bounded by side wall surfaces 20 and floor surface 22. The trench cavity in this structure is filled with a mass of silicon dioxide 24 that is in contact with the wall and floor surfaces 18, 20, 22, and is substantially void-free and of substantially uniform density throughout its bulk volume.

In preferred practice, the substantially void-free character of the silicon dioxide formed in the trench is readily confirmed by porosimetry, permeability criteria, SEM cross-sectioning, or other conventional techniques for morphological characterization to determine presence of voids.

The foregoing precursors and methodology of the invention enable effective formation of full fill trench structures with silicon dioxide that is curable under low temperature conditions to yield silicon dioxide of a substantially void-free condition with substantially uniform density throughout its bulk volume.

Another aspect of the invention relates to a Ge/Si oxide composition for gap filling in applications such as fill of memory device trenches. GeO₂ has a much lower viscosity than SiO₂. The invention in this aspect contemplates the use of a Si_(x)Ge_(1-x)O₂ to enable sufficient atomic rearrangement to occur for healing of the seam produced by coalescence of side-wall growth in the trench, thereby removing any non-uniform strain within the gap fill. This in turn enables a uniform removal rate to be achieved, with respect to cleaning chemistry exposure in subsequent processing of the device structure.

In the use of Si_(x)Ge_(1-x)O₂ for gap filling, the ratio of germanium to silicon in the film is advantageously in a range of from 0.005 to 0.25 (with x having a value in the formula Si_(x)Ge_(1-x)O₂ of 0.75 to 0.995), in order to appropriately minimize germanium content for achievement of acceptable dielectric properties.

In the use of such Ge/Si oxide compositions, only sufficient flow to fill the seam and remove strain non-uniformity is required, and high temperatures can be tolerated in the curing operation. These characteristics enable the amount of added germanium to be minimized, so that other film properties can be optimized. A preferred germanium precursor for such purpose is selected from among germanium alkoxides: R_(4-x)Ge(OR¹)_(x), R_(4-x)Ge(NR¹R²)_(x), and R_(4-x)GeH_(x); wherein x=0−4 and each R, R¹, R² is independently selected from among branched and unbranched C₁-C₆ alkyl, C₃-C₈ cycloalkyl, and C₆-C₁₃ aryl.

A preferred embodiment uses the tetra-alkoxygermanes, Ge(OMe)₄ (TMOG) or Ge(OEt)₄ (TEOG).

Using germanium alkoxides in a tetraethylorthosilicate (TEOS)/ozone (O₃) process has the advantage that film smoothness can be substantially improved. This factor is particularly important for gap fill, since the seam width is likely to be dependent on the roughness of the growth surfaces when coalescence occurs, as the sidewall growth elements meet one another.

The invention in another aspect relates to use of suppressors for bottom up gap fill. This aspect of the invention takes advantage of the fact that a deposition process characterized by a higher growth rate at the bottom of the trench than at the upper regions thereof will result in a reduced seam length, even offering the potential for elimination of the seam. The invention therefore contemplates suppression of deposition outside of the trench relative to the bottom of the trench, using a “suppressor” chemical species. The concentration of such suppressor can be reduced within the trench due to slower transport into the trench features relative to transport to the wafer surface. In order to generate low concentrations within the trench, some consumption of suppressor species is required, e.g. by decomposition or reaction in the gas phase or on the surface, such as may be effected by ozone-mediated oxidation.

In the tetraethylorthosilicate (TEOS)/ozone process, addition of methanol can be employed to planarize deposition profiles. Lower deposition rates can occur in very high aspect ratio structures due to accumulation of TEOS/O₃ reaction products, which in turn act to suppress growth. The TEOS/O₃ reaction products can include acetaldehyde and/or possible oxirane, and active species may include hydrocarbons with carbonyl functionality, as a product of oxidation of alcohols with ozone.

More generally, a wide variety of hydrocarbon species can be employed as suppressors to modify the deposited film profile within a trench. These include hydrocarbons with one or more carbonyl groups and/or one or more hydroxy groups.

As used herein, a “suppressor” is a species that reduces growth rate when introduced with precursor on a substrate.

FIG. 2 is a schematic representation of a microelectronic device structure 50 including a substrate 52 in which a trench 58, bounded by sidewalls 54 and floor 56, has been formed.

FIG. 2 shows suppressor being in the deposited material 56 including the precursor, and in FIG. 3, the formation of oxide 60 is shown on the main surface of the device structure 50 and in the trench 58. The lower transport rate of suppressor into the trench combined with suppressor consumption produces reduced suppressor concentrations at the bottom of the trench, with correspondingly increased oxide growth. This effect is stronger as the trench closes.

The ideal suppressor has a low gas diffusion rate and high molecular weight, and functions to strongly suppress film growth. The suppressor is consumed to effect depletion thereof, to an extent dependent on the degree of mass transport in the deposition system. Ideally, the suppressor is oxidized by ozone, and undergoes decomposition and reaction with tetraethylorthosilicate. Control of the oxide growth rate in the TEOS/O₃ process can be effected by surface reaction control. Preferred suppressor chemistries in specific applications include alcohol and alcohol oxidation products.

In using GeO₂/SiO₂ mixtures for gap fill of trenches, advantage is taken of the substantially lower viscosity of GeO₂/SiO₂, particularly under annealing conditions. In GeO₂/SiO₂ mixtures with minimal GeO₂/SiO₂ content, substantial strain relief is achievable as a result of the substantially lower viscosity of GeO₂/SiO₂, and at moderate GeO₂/SiO₂ content, sufficient flow character is present for healing of narrow seam structures in trench fill material. Germanium alkoxides can be used to achieve good GeO₂/SiO₂ mixtures for trench fill. The advantages of germanium in such GeO₂/SiO₂ mixtures, include, in relation to SiO₂ alone, higher flow at elevated temperatures, reduced moisture content, reduced film roughness and highly uniform chemical reactivity. The presence of germanium is appropriately limited to avoid undue etch rates in exposure to etchants such as hydrogen fluoride, and avoidance of leakage and breakdown strength issues in the cured fill material. Further, it may be desirable to limit or even avoid hydrogen environments in annealing operations, in order to avoid reduction of GeO₂/SiO₂ to GeO.

Reactions involved in sol-gel solution chemistry for formation of oxide fill material are set out below, including the reaction involved in the hydrolysis of TEOS:

and (poly) condensation of silanols:

In this reaction scheme, for every silanol bridge formed, one water molecule is consumed. The gel structure is dependent on reactant concentrations of TEOS and water, as well as pH of the deposited fill material. In acidic solutions, hydrolysis reaction tends to go to completion and less cross-linked chains are formed, with reesterification (reverse hydrolysis) being occasionally observed. In basic solution, more highly cross-linked structures are formed, with higher water concentrations promoting hydrolysis and impeding condensation, resulting in higher cross-linked density in the oxide material.

Concerning acid and base catalyzed hydrolysis, acid catalyzed hydrolysis proceeds by the following electrophilic mechanism involving H₃O⁺:

and base catalyzed hydrolysis proceeds by a nucleophilic reaction mechanism according to the following reaction:

The lower electron density on the silicon atoms as a result of silanol formation, in relation to alkoxy groups, produces a preferred attack of silicon centers with more silanol groups, in base catalyzed systems, and a preferred attack of silicon centers with more alkoxy groups, in acid catalyzed systems. Accordingly, there is a preference for chain extension in acidic solutions, and a preference for cross-linking in basic solutions.

In the TEOS/ozone system for deposition of oxide film material, the TEOS/ozone reaction products or oxidation products of the alkoxy ligand are set out in Table 1 below:

TABLE 1 Species Name CH₃COOH acetic acid CH₃CHO acetaldehyde HCOOH formic acid CH₂O formaldehyde CO carbon monoxide CO₂ carbon dioxide H₂O water ≡SiOH Silanol

In the TEOS/ozone process, alcohol addition yields enhanced flow characteristics, particularly when methanol is utilized. In the alcohol oxidation reaction, one equivalent of water and one equivalent of carboxylic acid are formed after double oxidation of the primary alcohol:

Alcohol addition in the TEOS/ozone process can utilize any suitable alcohol species, with the efficacy of specific alcohols being readily empirically determinable within the skill in the art, based on the disclosure herein. Alcohols such as methanol, formic acid, acetic acid and propionic acid may be used in specific embodiments of the invention. More generally, hydroxy-functional compounds may be used in the TEOS/O₃ process to enhance the character of the trench fill operation.

In specific implementations, hydroxy-functional species can include diols, e.g., ethylene glycol, and halogenated alcohols such as 2,2,2-tricholoroethanol.

Dicarboxylic acids can be formed from diols, by reactions such as the following:

Such use of polyol species produces stronger acid than the acid product formed from primary alcohols. Even stronger carboxylic acids can be formed from oxidation of halogenated alcohols, e.g., as shown by the following reaction. The pK_(a) of trichloracetic acid is 0.77.

Thus, the invention achieves improved gap filling of trench structures by use of germanium and silicon oxide mixtures, as well as by use of alcoholic or other suppressor species to avoid or minimize seam formation issues in the fill process.

The invention therefore overcomes the problems associated with the TEOS/ozone process in respect of seam formation in trench structures, particularly those with high aspect ratios.

More generally, the chemistry of silicon dioxide synthesis from alkoxide silicon precursors in aqueous solutions is fairly well understood. In the sol-gel process, the hydrolysis of TEOS can be either base or acid catalyzed to form a silanol group and two equivalents of ethanol. In a subsequent reaction step, two silanols condense to form a siloxane bridge and liberate one equivalent of water. After condensation, there are generally some remaining silanols and possibly unreacted alkoxy groups and reaction products. The result is a semi-solid mixture that is referred to as a gel. If SiO₂ is desired, the gel then is heated to remove byproducts and allow further condensation (calcination). The final structure, with respect to bond angles and defects, is determined by the solution pH, water and TEOS concentrations and calcination conditions.

The hydrolysis and condensation of TEOS and solutions proceeds by an electrophilic reaction mechanism in acid catalyzed solutions, as opposed to nucleophilic reaction in base catalyzed solutions. One consequence of this is that alkoxy groups on less hydrolyzed silicons are less stable with respect to condensation than those on more hydrolyzed silicon centers. This favors formation of chain structures. Conversely, base catalyzed condensation more readily occurs with silicon centers that have been hydrolyzed. This results in formation of more fully hydrolyzed species before condensation and therefore more cross-linking.

Water is consumed during hydrolysis and liberated during condensation. Accordingly, higher water concentrations promote hydrolysis and impede condensation. The result is higher cross-link density.

In the TEOS/ozone process, film formation also occurs by silanol formation followed by condensation of silanol groups to form siloxane bridges. Oxidation of alkoxy groups is also present (producing acetaldehyde, formaldehyde, CO, CO₂, and silanol groups). The presence of water and acid in TEOS/ozone processes affords the possibility of employing hydrolysis reactions to form SiO₂ films.

Oxidation of alcohol added to the TEOS/ozone process results in the presence of carboxylic acids. The acids formed from smaller primary alcohols have lower pK_(a) and may be more effective in catalyzing hydrolysis.

Accordingly, species that oxidize in the presence of ozone can be used to control the chemical reactions during a TEOS/ozone process. For example, double oxidation of alcohols produces both water and a carboxylic acid (acetic acid in the case of ethanol). Addition of the intermediate (acetaldehyde) can produce acid without forming water, and therefore can be employed to control the acid/H₂O ratio.

This has some advantages over direct addition of water and acid. Stable mixtures of alkoxide and alcohol/aldehydes or other organic species can be formed, whereas mixtures of acids and/or water and alkoxides will react over time. Liquid mixtures can allow for more accurate control of the ratio of reactant, and also allow in-situ generation of species that may not be stable enough for efficient delivery. Use of an aldehyde does not add water, and it therefore requires water from the condensation reaction to enable further hydrolysis to take place. Another potential advantage is flexibility in avoiding less safe and less stable alkoxides. For example, TEOS is preferred over tetramethoxysilane (TMOS), because TMOS is more toxic and more reactive to atmospheric contamination. TMOS, however, has better flowability. If an important difference is the presence of formic acid as the product of TMOS decomposition, then a similar result could be achieved with TEOS and methanol.

Stronger acids can more readily catalyze hydrolysis. These stronger acids can be formed from ethylene glycol or from halogenated alcohol such as trichloroethanol or trifluoroethanol. Oxidation of ethylene glycol results in oxalic acid (pK_(a)=1.23), and oxidation of trichloroethanol and trifluoroethanol results in trichloroacetic acid and trifluoroacetic acid, respectively (pK_(a)=0.77 and 0.30, respectively).

For single solution approaches, the additive employed in the TEOS/ozone process must be soluble in the alkoxide. In some cases, a co-solvent may be required to form a solution. For example, TEOS and ethylene glycol have very limited mutual solubility, but the addition of isopropyl alcohol allows the solution to be formed.

It will therefore be seen that the efficacy of the TEOS/ozone process can be substantially increased by addition of additives as disclosed herein.

The features and advantages of the invention are more fully shown by the following non-limiting examples of gap fill processes.

Gap Fill Process Examples

Deposition was carried out in an Applied Materials P5000 reactor with the TEOS/ozone process. Void fraction was found by measuring the void area in SEM cross-sections after cleaving and staining in 200:1 H₂O:HF. Stain times were chosen to result in 5 nm removal of SiO2 from blanket film witness pieces deposited in the same run. Results are set out below in the tables for Examples 1, 2 and 3.

Example 1

Parameter Value TEOS first Stabilize in TEOS 90 seconds before deposition Pressure 500Torr Susceptor Temperature 425 C Formulation: IPA/Methanol/TEOS 4:4:1 Liquid Flow 0.433 cc/min Ozonator feed gas 10SLM O2 + 100 ppm N2 Ozone Concentration 12% Susceptor spacing 420 mils Void % Annealed (800 C 30 min) 10.57 Void % As deposited 6.88 Rate 4.5 A/sec time for 2000A 444 seconds

Example 2

Parameter Value TEOS first Stabilize in TEOS 90 seconds before deposition Pressure 500Torr Susceptor Temperature 425 C Formulation: IPA:Ethanol:TMOG:TEOS 0.05:0.10:0.05:1 Liquid Flow 0.35 cc/min Ozonator feed gas 10SLM O2 + 100 ppm N2 Ozone Concentration 15% Susceptor spacing 420 mils Ge content (film) 2 atomic % Void % Annealed (800 C 30 min) 3.59% Void % As deposited 1.86 Rate 10 A/sec

Example 3

Parameter Value TEOS first Stabilize in TEOS 90 seconds before deposition Pressure 500Torr Susceptor Temperature 425 C Formulation: IPA:Ethanol:TMOG:TEOS 0.05:0.10:0.20:1 Liquid Flow 0.35 cc/min. Ozonator feed gas 10SLM O2 + 100 ppm N2 Ozone Conc 15% Susceptor spacing 420 mils Void % Annealed (800 C 30 min) 1.34% Void % As deposited 0.71 Rate 6 A/sec

While the invention has been has been described herein in reference to specific aspects, features and illustrative embodiments of the invention, it will be appreciated that the utility of the invention is not thus limited, but rather extends to and encompasses numerous other variations, modifications and alternative embodiments, as will suggest themselves to those of ordinary skill in the field of the present invention, based on the disclosure herein. Correspondingly, the invention as hereinafter claimed is intended to be broadly construed and interpreted, as including all such variations, modifications and alternative embodiments, within its spirit and scope. 

What is claimed is:
 1. A precursor composition, comprising: a germanium precursor; a silicon precursor; alcohol; and an oxidant.
 2. The composition of claim 1, wherein the composition is in a vapor phase.
 3. The composition of claim 1, wherein the germanium precursor comprises TMOG.
 4. The composition of claim 1, wherein the silicon precursor comprises tetraethylorthosilicate.
 5. The composition of claim 1, wherein the alcohol is selected from the group consisting of isopropyl alcohol, ethanol, and mixtures thereof.
 6. The composition of claim 1, wherein the oxidant comprises ozone.
 7. A method of processing a substrate including a trench or gap structure therein, comprising contacting the substrate with a composition according to claim 1, under conditions effecting deposition of a germanium- and silicon-containing oxide in the trench or gap structure.
 8. The composition of claim 1, wherein the germanium precursor comprises TMOG, the silicon precursor comprises tetraethylorthosilicate, the alcohol is selected from the group consisting of isopropanol, methanol, ethanol, and mixtures of two or more thereof, and the oxidant comprises ozone.
 9. A method of forming an oxide material in a trench structure of a substrate for filling thereof, said method comprising depositing on the substrate, for filling of the trench structure, a precursor composition including (i) oxide precursor material comprising germanium and silicon, and (ii) suppressor, to suppress seam formation, wherein said depositing is conducted at temperature below 400° C.
 10. The method of claim 9, wherein deposited oxide precursor material is cured under an ozone atmosphere.
 11. The method of claim 9, wherein the oxide precursor material comprises a germanium alkoxide.
 12. The method of claim 9, wherein said oxide precursor material is cured to form a GeSi oxide composition in said trench structure.
 13. The method of claim 9, wherein said depositing is conducted at temperature below 350° C.
 14. The method of claim 9, wherein the suppressor comprises hydroxyl functionality.
 15. The method of claim 9, wherein the suppressor comprises at least one hydroxyl functional suppressor, selected from the group consisting of alcohols, polyols and glycols.
 16. The method of claim 9, wherein the suppressor comprises alcohol.
 17. The method of claim 9, wherein the suppressor comprises a hydrocarbon with one or more carbonyl groups.
 18. The method of claim 9, wherein the suppressor is oxidized by ozone.
 19. A method of forming an oxide material in a trench structure of a substrate for filling thereof, said method comprising depositing tetraethylorthosilicate (TEOS) in a TEOS/ozone process to form silicon oxide material in the trench, with addition to the TEOS of an aldehyde effective to suppress deposition outside of the trench structure relative to the bottom of the trench.
 20. A method of forming an oxide material in a trench structure of a substrate for filling thereof, said method comprising depositing tetraethylorthosilicate (TEOS) in a TEOS/ozone process to form silicon oxide material in the trench, wherein said TEOS is deposited in a composition comprising ethylene glycol and isopropyl alcohol, wherein the ethylene glycol and isopropyl alcohol are effective to suppress deposition outside of the trench structure relative to the bottom of the trench structure. 